Suhu Tinggi Teflon PTFE Lembaran PTFE Lembaran Putih Dengan Pengisi Grafit / Karbon / Gangsa
1. intensiti voltan
2. voltan kerosakan tinggi
3. suhu operasi yang luas
Descriptio ns
Komponen yang dibuat dengan kepingan PTFE mempunyai ketahanan yang luar biasa terhadap suhu yang tinggi serta rendah, tindak balas kimia, kakisan, dan tekanan retak. Ciri-ciri elektrik dan rendah geseran PTFE menjadikannya bahan pilihan untuk beberapa aplikasi dan teknik pemprosesan yang berbeza.
LEMBARAN PTFE
|
ITEM
|
Result
|
Unit
|
|
Material
|
100% Virgin PTFE
|
|
|
Apparent density
|
2.10-2.30
|
g/ cm3
|
|
Tensile Strength
|
22-28
|
Mpa
|
|
Ultimate Elongation
|
250-300
|
%
|
|
Dielectric Strength
|
40
|
KV/mm
|
|
Tempature Resist
|
-180-+260
|
oC
|
|
PTFE Molded sheet Thickness
|
1.5mm-----120mm
|
|
Molded sheet
Length * width
|
Min Dimension=300x300mm, Max Dimension= 2000x2000mm Other sizes based on your requirements
|
|
PTFE Skived sheet thickness
|
0.1mm-----10.0mm
|
|
PTFE Skived sheet width(Max)
|
2700mm
|
Ciri-ciri utama
1.Haus tahan rintangan --- Ia dapat mengasah stok antara -180 ° C hingga + 260 ° C.
2. Hartanah yang tidak lekat --- Ia lebih mudah untuk menghapuskan resin, gelang, minyak dan benda melekit yang lain.
3. Kekayaan mekanikal yang baik tanpa sebarang herotan dan pekali geseran yang rendah.
4. Hartanah penebat yang hebat.
5. Bahan seperti karbon, grafit dan serat kaca boleh diisi.
6. Bahan-bahan yang berkualiti dan kitar semula boleh didapati
Ciri-ciri utama
|
Properties
|
Unit
|
Result
|
|
Apparent density
|
g/cm3
|
2.10-2.20
|
|
Tensile strength (min)
|
MPa
|
20
|
|
Ultimate elongation (min)
|
%
|
200
|
|
Residual Lubricant Content (max)
|
%
|
0.5
|
|
Dialectric Strength (min)
|
KV/mm
|
10
|
Imej:
Butiran:
Resin PTFE, dipenuhi dengan beberapa bahan pengisian, boleh memanjangkan hayat produk
dan mengukuhkan prestasi, contohnya: Grafit, Karbon, Serat kaca, gangsa
|
Glass Fiber:
|
Increases compressive strength, rigidity and wear.
Reduces creep and cold flow
Minimal effect on chemical and electrical properties
|
|
Carbon:
|
Increases compressive strength, hardness, wear, and load properties.
Good chemical resistance
Various types and amounts of carbon can be added to alter conductivity
|
|
Graphite:
|
Reduces coefficient of friction
Reduces initial wear
Increases strength
|
|
Molybdenum Disulfide:
|
Increases hardness, stiffness, and wear
Minimal effect on chemical and electrical properties
|
|
Bronze:
|
Increases hardness and wear resistance
Increases dimensional stability and compressive strength
Not suitable for corrosive or electrical applications
|
Aplikasi:
1.Besing terperangkap ke pemanasan sehingga rata untuk mengurangkan geseran .
2. Digunakan untuk membungkus kabel di bawah voltan tinggi dan suhu tinggi.
3. digunakan untuk menyegel bahagian-bahagian elektronik.
Kategori produk : Produk PTFE > Lembaran PTFE